- News
- Books
Featured Books
- smt007 Magazine
Latest Issues
Current IssueBox Build
One trend is to add box build and final assembly to your product offering. In this issue, we explore the opportunities and risks of adding system assembly to your service portfolio.
IPC APEX EXPO 2024 Pre-show
This month’s issue devotes its pages to a comprehensive preview of the IPC APEX EXPO 2024 event. Whether your role is technical or business, if you're new-to-the-industry or seasoned veteran, you'll find value throughout this program.
Boost Your Sales
Every part of your business can be evaluated as a process, including your sales funnel. Optimizing your selling process requires a coordinated effort between marketing and sales. In this issue, industry experts in marketing and sales offer their best advice on how to boost your sales efforts.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - smt007 Magazine
Solder Ball Joint Reliability with Electroless Ni/Pd/Au Plating – Influence of Electroless Pd Plating Film Thickness
June 20, 2017 | Yoshinori Ejiri, et al., Hitachi Chemical Co. LtdEstimated reading time: 4 minutes
Abstract
The influence of Pd film thickness in electroless Ni/Pd/Au plating on the solder ball joint reliability after reflow cycles and thermal aging was investigated by conducting a high-speed solder ball shear test. Sn-3.0Ag-0.5Cu (SAC305) was used as the solder ball in this study. On the basis of the solder joint reliability obtained after multiple reflow cycles and thermal aging, the optimum thickness of the Pd film was found to be 0.05–0.2 µm.
The covering property of electroless Pd plating film on the electroless Ni plating film was also investigated. We found that an electroless Pd plating film with a thickness of 0.02 µm or more covered the electroless Ni plating film adequately, and the solder ball joint reliability in this case was better than that with electroless Ni/Au plating. We consider that the shape of the intermetallic compounds (IMCs) is one of the factors that influence the solder joint reliability after multiple reflow cycles. Consequently, we inferred that the high adhesion at the dendrite layers of IMCs/solder interface resulted in excellent solder ball joint reliability after the reflow cycles. We consider that the thickness of the IMCs is one of the factors that influence the solder joint reliability after thermal aging. In (Cu, Ni, Pd)6Sn5 IMCs that contained trace amounts of Pd, the growth of the IMCs is prevented by Pd, resulting in excellent solder ball joint reliability after thermal aging.
Introduction
With the widespread use of portable electronic equipment, chip scale packages (CSPs) and ball grid arrays (BGAs) mounted on high-density printed circuit boards (PCBs) have become popular as semiconductor package assemblies. The CSPs and BGAs are connected to the PCBs using solder balls. Such connection methods require smaller connection areas and no metal leads, thus resulting in a lower ability to resist the stress relaxation than in the case of the traditional methods of connecting the leads of thin small outline packages (TSOP) and quad flat packages (QFPs). The connection methods employing solder balls, therefore, involve many problems related to joint reliability. Several studies on the reliability of solder ball joint connections with CSPs and BGAs are now in progress.
The conventional electrolytic Ni/Au plating is a mature technology that has long been used for surface finishing of package substrates. However, this technique cannot be applied to high-density package substrates, because it requires bus lines to each terminal and the necessary area for those lines. Therefore, electroless Ni/Au plating was adopted because it does not require bus lines. However, drop tests revealed that the reliability of ball joints prepared by this technique is insufficient. To solve this problem, electroless Ni/Pd/Au plating was adopted for surface finishing of the terminals of package substrates.
Recently, electroless Ni/Pd/Au plating is being offered as an alternative surface finishing process with high solder joint reliability and wire bondability. In the previous studies, the details regarding the influence of Pd thickness on solder joint reliability and IMC growth have not been provided. In this study, the influence of Pd film thickness on solder ball joint reliability was investigated to clearly identify the optimum thickness of the Pd film in electroless Ni/Pd/Au plating.
Experiments
Sample Preparation
A test pattern was formed on an epoxy resin copper cladding laminate (MCL-E-679F; Hitachi Chemical Co. Ltd) using the semi-additive method. The thicknesses of the board and copper pad were 0.6 mm and 25 μm, respectively. Then, solder resist was formed with a solder mask using a photo-definable type resist. The opening diameter of the ball pad was 0.45 mm. These test substrates were covered with electroless Ni/Au (ENIG: electroless Ni/immersion Au) and electroless Ni/Pd/Au (ENEPIG: electroless Ni/electroless Pd/immersion Au) plating. After applying flux, solder balls (SAC305) were attached to the test substrates and passed through a nitrogen-reflow furnace. The thickness of each plating film and the evaluation conditions are listed in Table 1.
Reliability Test on Solder Ball Joints (High-Speed Shear)
As shown in Figure 1, the distance between the shear tool tip and the package substrate was 50 μm. The shear speeds were 20, 200, and 500 mm/s.
Figure 1: Outline of solder-ball shear test.
A high-speed bond tester 4000HS (Dage Precision Industries, Ltd.) was used (Figure 2).
Figure 2: Externals of high-speed shear test equipment (DAGE 4000HS Bond Tester).
Page 1 of 2
Suggested Items
Vicor Power Orders Hentec Industries/RPS Automation Pulsar Solderability Testing System
04/24/2024 | Hentec Industries/RPS AutomationHentec Industries/RPS Automation, a leading manufacturer of selective soldering, lead tinning and solderability test equipment, is pleased to announce that Vicor Power has finalized the purchase of a Pulsar solderability testing system.
AIM Solder’s Dillon Zhu to Present on Ultraminiature Soldering at SMTA China East
04/22/2024 | AIMAIM Solder, a leading global manufacturer of solder assembly materials for the electronics industry, is pleased to announce that Dillon Zhu will present on the topic: Ultraminiature Soldering: Techniques, Technologies, and Standards at SMTA China East. This event is being held at the Shanghai World Expo Exhibition & Convention Center from April 24-25.
AIM to Highlight NC259FPA Ultrafine No Clean Solder Paste at SMTA Wisconsin Expo & Tech Forum
04/18/2024 | AIMAIM Solder, a leading global manufacturer of solder assembly materials for the electronics industry, is pleased to announce its participation in the upcoming SMTA Wisconsin Expo & Tech Forum taking place on May 7 at the Four Points by Sheraton | Milwaukee Airport, in Milwaukee, Wisconsin.
Hentec/RPS Publishes an Essential Guide to Selective Soldering Processing Tech Paper
04/17/2024 | Hentec Industries/RPS AutomationHentec Industries/RPS Automation, a leading manufacturer of selective soldering, lead tinning and solderability test equipment, announces that it has published a technical paper describing the critical process parameters that need to be optimized to ensure optimal results and guarantee the utmost in end-product quality.
Empowering Electronics Assembly: Introducing ALPHA Innolot MXE Alloy
04/16/2024 | MacDermid Alpha Electronics SolutionsIn the rapidly evolving electronics industry, where innovation drives progress, MacDermid Alpha Electronics Solutions is committed to setting a new standard. Today, we are pleased to introduce ALPHA Innolot MXE, a revolutionary alloy meticulously engineered to address the critical needs of enhanced reliability and performance in modern electronic assemblies.