- News
- Books
Featured Books
- smt007 Magazine
Latest Issues
Current IssueBox Build
One trend is to add box build and final assembly to your product offering. In this issue, we explore the opportunities and risks of adding system assembly to your service portfolio.
IPC APEX EXPO 2024 Pre-show
This month’s issue devotes its pages to a comprehensive preview of the IPC APEX EXPO 2024 event. Whether your role is technical or business, if you're new-to-the-industry or seasoned veteran, you'll find value throughout this program.
Boost Your Sales
Every part of your business can be evaluated as a process, including your sales funnel. Optimizing your selling process requires a coordinated effort between marketing and sales. In this issue, industry experts in marketing and sales offer their best advice on how to boost your sales efforts.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - smt007 Magazine
Via-in-Pad Plated over Design Considerations to Mitigate Solder Separation Failure
November 29, 2017 | S.Y. Teng, P. Peretta and P. Ton, Cisco Systems Inc.; and V. Kome-ong and W. Kamanee, Celestica ThailandEstimated reading time: 6 minutes
As signal speeds and performance requirements continue to rise, the use of advanced PCB technologies is becoming increasingly important. As a result, the via-in-pad plated over (VIPPO) structure has been adopted in many BGA footprint designs within the PCB. These VIPPO structures are preferred over the more traditional dog-bone pad structure in order to shrink signal path lengths, reducing two parasitic effects, capacitance and inductance, for improved highspeed performance.
Figure 1 illustrates how the VIPPO structure can influence those parasitic effects. The signal traces, which connect the BGA pads with the vias, act as inductors. Additionally, as high-speed designs typically have ground planes immediately below the outer layer, there is also a capacitive effect that is generated. With the VIPPO structure, the outer trace layer is eliminated, thereby cancelling both parasitic effects.
Figure 1: Dog-bone vs. VIPPO pad structure.
Figure 2 exhibits the VIPPO structure as compared with the VIPPO + backdrill (BD) structure. The use of backdrill with the VIPPO structure can eliminate the reflections within the unused portion of the via, which acts as a stub. The portion of the via indicated by the purple arrow is not in series with the signal path, but instead acts as a stub. Therefore, a portion of the signal is reflected back, creating an interference, which will degrade the high-speed signal performance. Hence, the purpose of the back-drill is to remove this “unused” portion of the via in order to eliminate the reflections for a cleaner signal.
Figure 2: VIPPO vs. VIPPO + backdrill structure.
With increased complexity of PCB designs for high-end networking products, the boards thicknesses are typically >120 mils and signal speeds are reaching 25 GHz and beyond. For these types of designs, backdrilling of the VIPPO structures becomes imperative.
It is also a common practice to mix VIPPO and non-VIPPO pad structures within a single BGA footprint, as indicated in Figure 3. The green lines indicate a high-speed signal trace (e.g., for differential pairs) on the outer layer. It is preferable from a signal integrity perspective, to route these signal lines on the outer layers of the PCB to take advantage of microstrip routing which has faster propagation speeds than stripline routing. Hence, these BGA pads do not require the use of VIPPO. These non-VIPPO pads are highlighted in red. Without any VIPPO structure, a zero stub length can be achieved, which is an extremely attractive option for the signal integrity engineer. Moreover, additional routing space is gained underneath the non-VIPPO pad. Unfortunately, these types of mixed footprint designs have a propensity for manufacturing defects during SMT assembly of BGA packages and can potentially expose the PCBA to field reliability risks if these defects escape manufacturing tests.
Figure 3: Mixed VIPPO/Non-VIPPO BGA Footprint.
Failure Mode and History
As a consequence of these advanced PCB technologies and complex board designs, a unique BGA solder joint failure mode has emerged during specific assembly conditions. This failure mode occurs when the bulk solder separates from the IMC during or just prior to reflow. This failure mode is of particular concern because the discontinuity is so small relative to the size of the solder joint itself that it cannot be detected via X-ray inspection methodologies. Furthermore, in many cases it is only a partial separation of the BGA solder joint and hence, it may not even be detected via ICT or functional test techniques. Without a robust methodology to screen for these defects, this presents an extremely high risk for potential escapes to the field.
Typically, this failure mode has been found on BGA packages with a 1 mm pitch or less BGA array and having a PCB footprint that includes a mixed VIPPO/non-VIPPO pad design. The solder separation occurs when the component is subjected to a secondary reflow, either during top-side SMT for bottom-side components or during rework of an adjacent, or mirrored, BGA component. Since the open occurs between the bulk solder and the IMC, it does not have the typical brittle solder joint fracture signature, which has a flat fracture interface through the IMC as shown in Figure 4. Instead, this failure mode exhibits more of a hot solder tear or separation type of failure mode, as the solder separates from the IMC leaving it intact.
Figure 4: Example of brittle fracture.
Figures 5 and 6 illustrate examples of both partial and complete solder separations. For these failures, the solder separation only occurs on the solder joints that use a VIPPO BGA pad and is typically adjacent to a solder joint(s) with a non-VIPPO BGA pad. In some cases, this type of failure mode has also been identified on a component having a full VIPPO BGA pad pattern on the PCB when there is also a pattern of VIPPO with deep backdrill (BD) within the footprint. Hence, the deep-backdrill VIPPO structures seem to mimic the behavior of the non-VIPPO pads so that it becomes comparable to a mixed VIPPO/non-VIPPO BGA pad footprint and again, induces solder separation in the solder joints on a VIPPO pad when subjected to a secondary reflow.
Page 1 of 2
Suggested Items
AIM to Highlight NC259FPA Ultrafine No Clean Solder Paste at SMTA Wisconsin Expo & Tech Forum
04/18/2024 | AIMAIM Solder, a leading global manufacturer of solder assembly materials for the electronics industry, is pleased to announce its participation in the upcoming SMTA Wisconsin Expo & Tech Forum taking place on May 7 at the Four Points by Sheraton | Milwaukee Airport, in Milwaukee, Wisconsin.
Hentec/RPS Publishes an Essential Guide to Selective Soldering Processing Tech Paper
04/17/2024 | Hentec Industries/RPS AutomationHentec Industries/RPS Automation, a leading manufacturer of selective soldering, lead tinning and solderability test equipment, announces that it has published a technical paper describing the critical process parameters that need to be optimized to ensure optimal results and guarantee the utmost in end-product quality.
Empowering Electronics Assembly: Introducing ALPHA Innolot MXE Alloy
04/16/2024 | MacDermid Alpha Electronics SolutionsIn the rapidly evolving electronics industry, where innovation drives progress, MacDermid Alpha Electronics Solutions is committed to setting a new standard. Today, we are pleased to introduce ALPHA Innolot MXE, a revolutionary alloy meticulously engineered to address the critical needs of enhanced reliability and performance in modern electronic assemblies.
New Book on Low-temperature Soldering Now Available
04/17/2024 | I-Connect007I-Connect007 is pleased to announce that The Printed Circuit Assembler’s Guide to… Low-temperature Soldering, Vol. 2, by subject matter experts at MacDermid Alpha Electronics Solutions, is now available for download.
Inkjet Solder Mask ‘Has Arrived’
04/10/2024 | Pete Starkey, I-Connect007I was delighted to be invited to attend an interactive webinar entitled “Solder Mask Coating Made Easy with Additive Manufacturing,” hosted by SUSS MicroTec Netherlands in Eindhoven. The webinar was introduced and moderated by André Bodegom, managing director at Adeon Technologies, and the speakers were Mariana Van Dam, senior product manager PCB imaging solutions at AGFA in Belgium; Ashley Steers, sales manager at Electra Polymers in the UK; and Dr. Luca Gautero, product manager at SUSS MicroTec Netherlands.