I managed to catch up with George Milad of Uyemura at the recent SMTA International conference, which wasn’t easy to do. But he did take a few minutes to fill me in on his schedule for the week and it certainly was packed, with a tutorial, presentations and IPC committee meetings.
Patty Goldman: Hi, George, it’s great to see you again—about twice a year, right? Let’s talk a little bit about what you’re presenting here at the SMTAI conference.
George Milad: I have had a very busy schedule. Yesterday I gave a presentation, a four-hour tutorial, and I will never do that again. To stand up and talk for four complete hours, it's very challenging staying alert and relevant and keeping the audience’s attention and making sure you're delivering value, because these people paid money to sit in that meeting. That was very challenging but it went very well and I'm happy. I get energized by the feedback from the attendees in the class, but then when I got back to my hotel, I was trying to listen to the presidential debate and I fell asleep after the first five minutes. (Laughs)
Goldman: I heard it was not that exciting of a debate, anyhow. But that does sound exhausting. How many people were in your audience?
Milad: We had approximately 15 people who signed up and paid money. That is very rewarding, because I gave the same training course at PCB West and I think if you signed up it was free, and I had three people show up. I talked forever for three people and it kills your energy, but this one was a very rewarding experience.
Goldman: You imparted a lot of knowledge.
Milad: Yes, they thought it was good. They filled in the forms and so I'll get some feedback from SMTA. Then first thing in the morning tomorrow I'm going to talk about the “Via Fill Copper Plating Process” and what it takes to optimize the via fill process. I-Connect007 published an article along these lines recently and this is basically the same concept but in the form of a presentation rather than an article.
Then I have the IPC 4-14 Plating Processes subcommittee meeting. Our committee meetings are not so critical because we do our work by conference call.
Goldman: Yes, I was very impressed when we talked about that before. I've been very impressed with how you guys conduct those meetings every…how many weeks?
Milad: Every other week.
Goldman: You get a lot accomplished that way.
Milad: Indeed. Then you set things in motion, and you say, "Okay, we need to just make a test vehicle (TV) ." Somebody manufactures it and then every couple of weeks we find out the status, and when the TV is complete, we send it out to people to plate it. Then we send it back out for evaluation We're always following these activities and evaluating results, and then we begin to write the specification and get interaction from people who sometimes like what's being written or some people take a strong objection to what's being written. And for good reason—I'm not saying they will just object for the sake of objecting.
For this, we were rewriting the ENIG spec. We wanted to set the upper limit for ENIG. It was written in 2002.
Goldman: That's a long time ago.
Milad: Yeah, 14 years later we're revising the specification. In 2002, we agreed that gold should be a minimum of two microinches. We did not put an upper limit, but we wrote that it should typically be 3−5 microinches. Typically, 3−5 is not the specification. Minimum of 2 microinches is the specification. Anybody who read the specification said the IPC calls for 3−5 μins, which was a horrible thing. We never called for 3−5 μins and it created a lot of problems.
Now, we’ve come back and we are redefining the gold thickness. We put the lower limit of 1.6 μins instead of two. Then, we wanted to put an upper limit. We tried very hard to pass 3.2 μins as the upper limit. We got a lot of resistance from manufacturers who do ENIG surface finish for the medical industry. They called for a minimum of 3.0 μins. They are the biggest printed circuit shop in the United States, I don't feel I should mention their name, but they said they have medical customers who will require a 3.0 μins minimum. We wanted to put 3.2 as the maximum, leaving no room at all to work between 3.0 and 3.2 μins. They kept arguing and finally we conceded and we put 4.0 μins as the upper limit. That is what the new specs will say, 1.6 to 4.0 μins. This is the first time we put an upper limit and as far as the 3−5 μins, we're hoping that will go by the wayside.
Goldman: I imagine it is a problem to put too much down, isn't it?
Milad: Absolutely. The problem with putting too much down is you're staying in the gold bath for a prolonged amount of time and that gives a lot of opportunity for nickel corrosion, or black pad. It's always been our objective to say, “Don't do that. You need only 2.0 μins. Get them deposited on the nickel and get out of the bath. There is no reason to stay any longer.”
It's not that it's guaranteed that if you stay longer in the bath that you're going to have corrosion, but if the nickel is a little bit compromised, it's not the perfect nickel, and you stay too long you will get corrosion. If you have the perfect nickel, it can withstand prolonged dwell in the gold bath, but nobody makes perfect nickel 100% of the time. We felt it's very important to restrict the gold thickness.
Goldman: This corrosion you're talking about is black pad, right?
Milad: Yes, the nickel corrosion and black pad are synonymous. If it is too extensive, then the pad is not going to solder, and the whole objective of the ENIG finish is that it’s a solderable finish. That's the story there. We don't want you to stay too long in the gold baths.
We also are including a corrosion chart in this new revision of the ENIG specification, which was quite challenging because when you have corrosion and you do a cross-section, it appears as spikes. When you look at a cross-section under 1000x magnification and you see less than 10 spikes in the field of view, that's acceptable. If you have more than 10 spikes, that's not acceptable. If the spikes are joined together, meaning they blend, one spike runs into the other, that's not acceptable. If the spike is too deep, that's not acceptable. We specified that and we ran into a huge tizzy of argumentation.
Is it 10? Is it 8? Is it 9? Is it 11? Is it 12? We finally said that we're just going to define what is acceptable and we're going to define what is rejectable. We're going to admit that there is a gray area between acceptable and rejectable.
Goldman: Yes, like saying 10 is good but 11 is bad? It seems that people might say, "Wait a minute. That's not that bad, is it?”
Milad: Yeah, so we decided to leave everything in between for the buyer and the manufacturer to sort out. If it's less than 10, we don't want any argument. We want this to be acceptable.
Page 1 of 2
Suggested Items
AIM to Highlight NC259FPA Ultrafine No Clean Solder Paste at SMTA Wisconsin Expo & Tech Forum
04/18/2024 | AIMAIM Solder, a leading global manufacturer of solder assembly materials for the electronics industry, is pleased to announce its participation in the upcoming SMTA Wisconsin Expo & Tech Forum taking place on May 7 at the Four Points by Sheraton | Milwaukee Airport, in Milwaukee, Wisconsin.
Hentec/RPS Publishes an Essential Guide to Selective Soldering Processing Tech Paper
04/17/2024 | Hentec Industries/RPS AutomationHentec Industries/RPS Automation, a leading manufacturer of selective soldering, lead tinning and solderability test equipment, announces that it has published a technical paper describing the critical process parameters that need to be optimized to ensure optimal results and guarantee the utmost in end-product quality.
Empowering Electronics Assembly: Introducing ALPHA Innolot MXE Alloy
04/16/2024 | MacDermid Alpha Electronics SolutionsIn the rapidly evolving electronics industry, where innovation drives progress, MacDermid Alpha Electronics Solutions is committed to setting a new standard. Today, we are pleased to introduce ALPHA Innolot MXE, a revolutionary alloy meticulously engineered to address the critical needs of enhanced reliability and performance in modern electronic assemblies.
New Book on Low-temperature Soldering Now Available
04/17/2024 | I-Connect007I-Connect007 is pleased to announce that The Printed Circuit Assembler’s Guide to… Low-temperature Soldering, Vol. 2, by subject matter experts at MacDermid Alpha Electronics Solutions, is now available for download.
Inkjet Solder Mask ‘Has Arrived’
04/10/2024 | Pete Starkey, I-Connect007I was delighted to be invited to attend an interactive webinar entitled “Solder Mask Coating Made Easy with Additive Manufacturing,” hosted by SUSS MicroTec Netherlands in Eindhoven. The webinar was introduced and moderated by André Bodegom, managing director at Adeon Technologies, and the speakers were Mariana Van Dam, senior product manager PCB imaging solutions at AGFA in Belgium; Ashley Steers, sales manager at Electra Polymers in the UK; and Dr. Luca Gautero, product manager at SUSS MicroTec Netherlands.